Firanita, Yuani (2026) Sintesis dan Karakterisasi Hidroksiapatit dari Cangkang Kepiting dengan Metode Sol Gel. Undergraduate thesis, UPN Veteran Jawa Timur.
![[img]](https://repository.upnjatim.ac.id/style/images/fileicons/text.png) |
Text (cover)
22031010231-Cover.pdf Download (3MB) |
|
Text (bab 1)
22031010231-bab1.pdf Download (293kB) |
|
Text (bab 2)
22031010231-bab2.pdf Restricted to Repository staff only until 21 July 2028. Download (387kB) |
|
Text (bab 3)
22031010231-bab3.pdf Restricted to Repository staff only until 21 July 2028. Download (486kB) |
|
Text (bab 4)
22031010231-bab4.pdf Restricted to Repository staff only until 21 July 2028. Download (433kB) |
|
Text (bab 5)
22031010231-bab5.pdf Download (231kB) |
|
Text (daftar pustaka)
22031010231-daftarpustaka.pdf Download (247kB) |
|
Text (lampiran)
22031010231-lampiran.pdf Restricted to Repository staff only Download (668kB) |
Abstract
This study aimed to synthesize and characterize hydroxyapatite from crab shell waste using the sol-gel method and to investigate the effects of pH and sintering temperature on the resulting product. Crab shells were utilized as a calcium source due to their high CaCO₃ content and potential as an environmentally friendly raw material. pH variations ranging from 7 to 11 and sintering temperatures of 400–800°C were applied during the synthesis process. The results showed that the hydroxyapatite yield ranged from 51–65%. XRF analysis indicated that the optimum condition was obtained at pH 7 and a sintering temperature of 800°C, with a Ca/P ratio of 2.67. This value was still higher than the standard ratio of 1.67, which was presumably caused by the high calcium content and the presence of Mg²⁺ ions. XRD analysis confirmed the formation of hydroxyapatite however, the product was not completely pure due to the presence of a secondary phase, namely Calcium Magnesium Hydrogen Phosphate, although several diffraction peaks corresponded to the standard hydroxyapatite pattern. This study demonstrates that crab shell waste has potential as a raw material for hydroxyapatite production through proper control of the synthesis conditions.
| Item Type: | Thesis (Undergraduate) | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
||||||||
| Subjects: | T Technology > T Technology (General) T Technology > TP Chemical technology T Technology > TP Chemical technology > TP155 Chemical engineering |
||||||||
| Divisions: | Faculty of Engineering > Departement of Chemical Engineering | ||||||||
| Depositing User: | Yuani Firanita | ||||||||
| Date Deposited: | 23 Jul 2026 04:16 | ||||||||
| Last Modified: | 23 Jul 2026 04:16 | ||||||||
| URI: | https://repository.upnjatim.ac.id/id/eprint/53949 |
Actions (login required)
 |
View Item |