Novianah, Delia Indah (2025) Sintesis Nanokristal Selulosa dari Sekam Padi Menggunakan Hidrolisis Asam Nitrat. Undergraduate thesis, UPN Veteran Jawa Timur.
![[img]](https://repository.upnjatim.ac.id/style/images/fileicons/text.png) |
Text (COVER)
21031010108_Cover.pdf Download (3MB) |
|
Text (BAB I)
21031010108_Bab 1.pdf Download (112kB) |
|
Text (BAB II)
21031010108_Bab 2.pdf Restricted to Repository staff only until 16 September 2028. Download (353kB) | Request a copy |
|
Text (BAB III)
21031010108_Bab 3.pdf Restricted to Repository staff only until 16 September 2028. Download (239kB) | Request a copy |
|
Text (BAB IV)
21031010108_Bab 4.pdf Restricted to Repository staff only until 16 September 2028. Download (836kB) | Request a copy |
|
Text (BAB V)
21031010108_Bab 5.pdf Download (105kB) |
|
Text (DAFTAR PUSTAKA)
21031010108_Daftar Pustaka.pdf Download (182kB) |
|
Text (LAMPIRAN)
21031010108_Lampiran.pdf Restricted to Repository staff only until 16 September 2028. Download (1MB) | Request a copy |
Abstract
Rice husk residue has excellent potential as a raw material for making cellulose nanocrystals because of its relatively high cellulose content. This research focuses on determining the most effective hydrolysis conditions, especially the reaction time and nitric acid (HNO₃) content, in the synthesis of cellulose nanocrystals. This study also aims to determine the effect of variations in nitric acid concentration and hydrolysis time on the amount of product produced (yield) and the final size of cellulose nanocrystals. The process of making these nanocrystals involves three main stages, namely the removal of lignin using a 17,5% NaOH solution, followed by annealing using a 10% H₂O₂ solution, and finally breaking the cellulose bonds (acid hydrolysis) with a concentrated nitric acid solution of between 2% and 6% for different time periods (30 to 15 minutes). Product characterization using FT-IR and SEM has been carried out to confirm the presence of cellulose and determine the size of the nanocrystals formed. Experimental results show that the smallest cellulose crystal size achieved is between 0,93 to 65,10 μm, which was obtained through hydrolysis using 6% nitric acid for 150 minutes.
| Item Type: | Thesis (Undergraduate) | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
||||||||
| Subjects: | T Technology > TP Chemical technology > TP155 Chemical engineering | ||||||||
| Divisions: | Faculty of Engineering > Departement of Chemical Engineering | ||||||||
| Depositing User: | Delia Indah Novianah | ||||||||
| Date Deposited: | 04 Dec 2025 07:28 | ||||||||
| Last Modified: | 04 Dec 2025 07:28 | ||||||||
| URI: | https://repository.upnjatim.ac.id/id/eprint/47278 |
Actions (login required)
 |
View Item |