PEMBUATAN KARBON AKTIF SERBUK GERGAJI KAYU JATI MENGGUNAKAN AKTIVATOR H3PO4 DAN MODIFIKASI TiO2

Wijaya, Lestari Sriani (2022) PEMBUATAN KARBON AKTIF SERBUK GERGAJI KAYU JATI MENGGUNAKAN AKTIVATOR H3PO4 DAN MODIFIKASI TiO2. Undergraduate thesis, UPN Veteran Jawa Timur.

[img]
Preview
Text
18031010156-cover riset fixx.pdf

Download (797kB) | Preview
[img]
Preview
Text (bab 1 pendahuluan)
18031010156-BAB I PENDAHULUAN.pdf

Download (145kB) | Preview
[img]
Preview
Text (bab 2 tinjauan pustaka)
18031010156-BAB II TINJAUAN PUSTAKA.pdf

Download (370kB) | Preview
[img] Text (bab 3 metodologi penelitian)
18031010156-BAB III METODOLOGI PENELITIAN.pdf
Restricted to Registered users only until 24 July 2024.

Download (227kB)
[img] Text (bab 4 hasil dan pembahasan)
18031010156-BAB IV HASIL DAN PEMBAHASAN.pdf
Restricted to Registered users only until 24 July 2024.

Download (622kB)
[img]
Preview
Text (bab 5 kesimpulan dan saran)
18031010156-BAB V KESIMPULAN DAN SARAN.pdf

Download (133kB) | Preview
[img]
Preview
Text (daftar pustaka)
18031010156-DAFTAR PUSTAKA LESTARI.pdf

Download (280kB) | Preview
[img] Text (lampiran)
18031010156-LAMPIRAN LESTARI.pdf
Restricted to Registered users only until 24 July 2024.

Download (745kB)

Abstract

Activated charcoal is a charcoal material that has pores with a large surface area so it is often used. The purpose of this experiment is to determine the process of making teak wood powder using H3PO4 activator and titanium dioxide modification. The process used in the manufacture of teak wood powder activated charcoal using the pyrolysis process. Sawdust was weighed with an initial weight ratio of 200 grams, 300 grams and 400 grams. The activation process for activated charcoal from teak wood powder is chemically activated and without activation. In the chemical activation process, activated charcoal obtained from the pyrolysis process is immersed using phosphoric acid activation agent with concentration ratios of 5%, 10%, 15%, 20% and 25%. After the activation process was carried out using phosphoric acid, then modification or addition of titanium dioxide was carried out in a ratio (4:1). This study gave optimum results at an initial weight of 200 grams with a concentration of 15%, the moisture content was 8.75% and the ash content was 15.84%. EDX test results obtained that the chemical components of activated charcoal are charcoal (C) by 22.27% by weight, Oxygen (O) by 33.26% by weight, Aluminum (Al) by 0.93% by weight, Silicon (Si) by 2, 01% by weight, Phosphorus (P) by 3.12% by weight and Titanium (Ti) by 38.4% by weight.

Item Type: Thesis (Undergraduate)
Contributors:
ContributionContributorsNIDN/NIDKEmail
Thesis advisorKurniati, ElyNIDN0718106402UNSPECIFIED
Subjects: T Technology > TP Chemical technology > TP155 Chemical engineering
Divisions: Faculty of Engineering > Departement of Chemical Engineering
Depositing User: Unnamed user with email 18031010156@student.upnjatim.ac.id
Date Deposited: 25 Jul 2022 08:43
Last Modified: 25 Jul 2022 08:43
URI: http://repository.upnjatim.ac.id/id/eprint/8084

Actions (login required)

View Item View Item